Submerged Arc Welding Wire Aws EL8

GUJIN® is a kind of low manganese low Submerged Arc Welding Wire Aws El8. It is matched with high manganese and high silicon type fluxes. Insensitive to rust on the base metal, excellent bead forming and slag separation. It is the most commonly used submerged arc welding wire. Monoles or dipoles. Can be used for AC/DC.

Send Inquiry

Product Description

GUJIN® is the professional manufacturer, we would like to provide you Submerged Arc Welding Wire Aws El8 and we will offer you the best after-sale service and timely delivery. GJ-H08A is a kind of low manganese low silicon type carbon steel submerged arc welding wire. It is matched with high manganese and high silicon type fluxes. Insensitive to rust on the base metal, excellent bead forming and slag separation. It is the most commonly used submerged arc welding wire. Monoles or dipoles. Can be used for AC/DC.

Product

Name

Standard and steel grade

Dia

(mm)

Chemical composition of welding wire

AWS

DIN/BS

H08A

EL8

2.0-5.0

≤1.0

0.30-0.55

≤0.03

≤0.20

≤0.30

≤0.20

Typical Mechanical Properties of The Deposited Metal (Using with Flux SJ-301)
Yield Strength (Mpa)	Tensile Strength (Mpa)	Elongation (%)	Impact test
			Temperature (℃)	Impact Energy （J）
360	450	29	-20	80

Uses: Used withAgglomerated submerged arc welding flux SJ-301 andSJ-501. It is used for high-speed welding and filler welding of 50kg class base metal.

Packing terms
Diameter	2.0mm	2.4mm	4.0mm	4.8mm
Small coil(Inner Dia 300mm) 25kg	√	√	√	√
Large coil(Inner Dia ,550mm 630mm) 100kg,150kg,200kg,250kg,350kg	√	√	√	√
Metal spool(Inner Dia 300mm) 25kg	√	√	√	√